西北地 区高性能风积沙固化剂的研制及工程应用

作者:吴克雄1,3,4,宋向荣2,李顺凯1,3,4,胡锦轩1,3,4,王志亮1,3,4,刘崇敬2

关键字:西北地区,高性能,风积,沙,固化剂,的,研制,及,

 
(1.中交武 汉港湾工程设计研究院有限公司,湖北 武汉  430000;
2.中交第 二航务工程局有限公司,湖北 武汉  430040;
3.海工结 构新材料及维护加固技术湖北省重点实验室,湖北 武汉  430000;
4.长大桥 梁建设施工技术交通行业重点实验室,湖北 武汉  430000)
    摘要:针对目 前固化风积沙存在的力学性能、收缩性能、耐水性 能等综合性能不佳的问题,研制了 一种高性能风积沙固化剂,对固化风积沙的7 d无侧限抗压强度、收缩应变、软化系数进行了测试,并与不 同种类固化剂的固化效果进行了对比。结果表明:聚乙烯 醇可大幅提高固化风积沙的抗压强度,但会降 低固化风积沙耐水性能,通过乳 液的添加可显著改善其耐水性能,纳米材 料可显著改善固化风积沙的收缩性能。与其它 种类固化剂相比,制备的 高性能风积沙固化剂在力学性能、收缩性能、耐水性 能上均有较大的优势,目前已 成功应用于北仙一级公路,其各项 路用性能均符合相关规范要求。
    关键词:风积沙;力学性能;收缩性能;耐水性能;纳米材料
    中图分类号:TU472.5        文献标识码:A        文章编号:1001-702X(2020)10-0060-05
 
Development of high performance curing agent of aeolian sand in northwest China and its engineering application
WU Kexiong1,3,4,SONG Xiangrong2,LI Shunkai1,3,4,HU Jinxuan1,3,4,WANG Zhiliang1,3,4,LIU Chongjing2
(1.CCCC WuHan Harbour Engineering Design and Research Co. Ltd.,Wuhan 430000,China;
2.The Second Harbor Engineering Company,Wuhan 430040,China;
3.Hubei Key Laboratory of Advanced Materials & Reinforcement Technology Research for Marine Environment Structures,Wuhan 430000,China;
4.Key Laboratory of Large-span Bridge Construction Technology,Wuhan 430000,China)
    Abstract:Aiming at the problem of poor comprehensive performance of mechanical properties,shrinkage performance and water resistance of cured aeolian sand,a high performance aeolian sand curing agent was developed and a series of experimental studies were carried out,the aeolian sand of unconfined compressive strength of 7 days,shrinkage strain and softening coefficient were tested and compared with the curing effects of different kinds of curing agents. The results showed that: polyvinyl alcohol can greatly improve the compressive strength of the mixture,but it will reduce the water resistance of mixture,the water resistance can be significantly improved by the addition of emulsion,and nanomaterials can significantly improve the shrinkage of the mixture. Compared with other types of curing agents,it has great advantages in mechanical properties,shrinkage properties and water resistance. It is an aeolian sand curing agent with excellent comprehensive performance. It has been successfully applied to the Beixian First Class Highway,and its various road performance indicators meet the requirements of the standard.
    Key words:aeolian sand,mechanical properties,shrinkage properties,water resistance,nanomaterials